Marjunus, Roniyus and Firdaus, Iqbal and Manurung, Posman (2021) Synthesis and Characterization of TiO2 Thin Film Based on Iron Sand of Lampung Province - Indonesia. In: International Symposium on Physics and Applications (ISPA 2020), 17-18 December 2020, Surabaya, Indonesia.

[img]
Preview
Text
Marjunus_2021_J._Phys.__Conf._Ser._1951_012002.pdf

Download (728kB) | Preview
Official URL: https://iopscience.iop.org/article/10.1088/1742-65...

Abstract

This study aims to make a thin layer of TiO2 based on ilmenite stored in iron sand of Lampung Province, Indonesia. The TiO2 powder, which was used to make the thin layer, was obtained from the extraction of iron sand using the leaching method with a purity of 60,7%. The preparation of TiO2 thin layers was carried out by the Chemical Bath Deposition (CBD) method with immersion time variations of 2, 3, 4, and 5 hours for samples A, B, C, and D respectively. Afterward, the samples were calcined at 500˚C for 4 hours. The characterizations involved XRay Diffraction (XRD), Scanning Electron Microscope (SEM), X-Ray Fluorescence (XRF), and four-point probe to measure the resistivity of the film. The XRD results in samples A (immersion time 2 hours) and D (immersion time 5 hours) show that the amorphous phase still dominates even though the diffraction peaks indicate that the presence of crystals has started to grow at several angles of scattering. The identification results of the phase presence show that the thin layer of TiO2 at sample D is the brookite phase. The results of characterization using SEM show that the surface of the TiO2 thin layer forms a porous structure. The average thickness of the thin film at sample B based on SEM analysis is 1.9 μm. The electrical resistivity increased with an increasing immersion time

Item Type: Conference or Workshop Item (Paper)
Subjects: Q Science > QC Physics
Divisions: Fakultas Matematika dan Ilmu Pengetahuan Alam (FMIPA) > Prodi Fisika
Depositing User: Iqbal Firdaus
Date Deposited: 27 Jul 2021 04:45
Last Modified: 27 Jul 2021 04:45
URI: http://repository.lppm.unila.ac.id/id/eprint/33259