Sugiyanto, Sugiyanto (2020) Penilaian: DEGRADATION OF MILD STEEL IN ETHANOL BURNING ENVIRONMENT: OXIDATION KINETICS AND MICROSTRUCTURAL ASPECT. LPPM Unila.

[img]
Preview
Text
Penilaian J Geomate - Degradation 4 reviewer.pdf

Download (876kB) | Preview

Abstract

ABSTRACT: The isothermal oxidation of an AISI 1005 steel (mild steel) in water vapour and CO 2 mixtures containing environments resulted from ethanol combustion had been investigated for exposure times ranging from 1 hour to 49 hours at elevated temperatures (700 °C, 750 °C and 800 °C). The steel was also oxidized in dry air for comparison. In water vapour and CO2 environments, mild steel underwent a significant degradation in term of the oxidation kinetics compared with those of steel oxidized in dry air environment. This finding is supported by a lower activation energy for steel oxidized in ethanol combustion products (199 kJ/mol) than that of for steel oxidized in dry air (224 kJ/mol). In addition, the breakaway oxidation was found for the steel subjected to ethanol combustion products at 800 °C. The carbon deposited in the magnetite layer was believed to lead the breakaway oxidation after an exposure time for 4 hours. A typical iron oxide growing on steel oxidized in ethanol combustion product is a pyramidal grain structures with compact scale but in dry air environment the iron rich oxide growing on the steel surface is a wrinkle characteristic displaying hollow structures at 700 °C and rough-grained oxide structures at 750–800 °C.

Item Type: Other
Subjects: T Technology > TJ Mechanical engineering and machinery
T Technology > TN Mining engineering. Metallurgy
Depositing User: Dr. SUGIYANTO ,M.T.
Date Deposited: 13 May 2020 04:41
Last Modified: 13 May 2020 04:41
URI: http://repository.lppm.unila.ac.id/id/eprint/19579

Actions (login required)

View Item View Item