Sulistiyo, Septian Tri and Situmeang, Rudy T.M (2015) Characteristics of nanosize spinel Ni0.9Fe2Co0.1O4 prepared by a sol-gel method using pectin as an emulsifying agent. In: The 1st International Conference on Sciences and Science Education, November 2015, Salatiga.

Rudy and Septhian.pdf

Download (2MB) | Preview
Official URL:


Ni0.9Fe2Co0.1O4 nanomaterial has been prepared using a sol -gel method. Preparation of material was carried out by dissolving nitrate salts of iron, cobalt and nickel, in pectin solution and then the sample was stirred thoroughly using magnetic stirrer while adjusting pH to 11. After freeze-drying process, the sample was subjected to calcination treatment and subsequently characterized using the techniques of X-ray diffraction(XRD), Scherrer Methods, FTIR and DT-TG analysis. The results of XRD characterization indicated that materials consist of two crystalline phases, such as CoFe2O4 and NiFe2O4. These two crystalline phases are superimposed. DT-TGA result showed that spinel Ni0.9Fe2Co0.1O4formed above 400oC. Then, PSA determination proved that the grain size of spinel ferrites is a range of 30–95.2 nm as much as 21%. Crystallite size calculation using the Scherrer equation, proved that the size is 31.95 nm. Its size increased as temperature calcination augmaunted.

Item Type: Conference or Workshop Item (Speech)
Subjects: Q Science > QD Chemistry
Divisions: Fakultas Matematika dan Ilmu Pengetahuan Alam (FMIPA) > Prodi Magister Ilmu Kimia
Depositing User: Dr. Rudy Tahan Mangapul Situmeang
Date Deposited: 06 Nov 2018 03:07
Last Modified: 06 Nov 2018 03:07

Actions (login required)

View Item View Item