Hermida, Lilis and Abdullah, Ahmad Zuhairi and Mohammed, Abdur Rahman (2018) FT-IR and TGA of MCF Silica-Supported Nickel Catalyst. Journal of Materials and Environmental Sciences, 9 (8). pp. 2328-2333. ISSN 2028-2508

[img] Archive
256-JMES-3471-Hermida.pdf - Published Version

Download (427kB)
Official URL: http://www.jmaterenvironsci.com/index.html

Abstract

In the present study, active site–support bonds in calcined and reduced catalysts of MCF silica-supported nickel catalysts were investigated using FTIR analyses. FTIR results show the presence of nickel phyllosilicate bonds (-O-Ni-O-Si) in the calcined catalysts.However, nickel phyllosilicate bonds were not detected in the reduced catalysts indicating that nickel phyllosilicate bons were absence after reduction process. FTIR results confirmed the presence of Ni-O-Si bond in the reduced catalysts. TGA analyses were also carried to investigate catalyst stability in terms of weight loss, thermal behaviour and structural destruction. According to the TGA results, dried catalyst of MCF silica-supported nickel catalyst showed weight loss of around 9% in a region from room temperature to 300 o C and weigh loss of 6% at above 300 o C. Weight loss from room temperature to 300 o C was ascribed to desorption of physisorbed and chemisorbed water. Meanwhile, weight loss at above 300 o C could be due to slow decompositions of nickel phyllosilicate to the formation of nickel oxide.

Item Type: Article
Subjects: T Technology > TP Chemical technology
Divisions: Fakultas Teknik (FT) > Prodi Teknik Kimia
Depositing User: Dr. LILIS HERMIDA
Date Deposited: 06 Nov 2018 03:06
Last Modified: 06 Nov 2018 03:06
URI: http://repository.lppm.unila.ac.id/id/eprint/9496

Actions (login required)

View Item View Item