Rustamaji, Heri and Prakoso, Tirto and Devianto, Hary and Widiatmoko, Pramujo and Nurdin, Isdiriayani (2022) Design, Fabrication, and Testing of Supercapacitor Based on Nanocarbon Composite Material. ASEAN Journal of Chemical Engineering, 22 (1). pp. 19-32. ISSN 2655-5409
|
Text
2022 Rustamaji_Design, Fabrication, and Testing of Supercapacitor Based on.pdf Download (1MB) | Preview |
Abstract
This research investigates the design, fabrication, and testing of single-cell and module supercapacitors. The supercapacitor consists of carbon nanocomposites, which contain activated carbon (AC), multiwall carbon nanotubes (MWCNT), and graphene (GR). The coin and pouch cell type supercapacitors were manufactured with AC: MWCNT: GR composite electrodes in a ratio of 70:20:10 weight percent. Meanwhile, the electrochemical characterization showed that the highest capacitance values for single coin and pouch cells were 32.13 F g-1 and 5.3 F g-1 , respectively, in 6 M KOH electrolyte at a scan rate of 2 mV s-1. Furthermore, the power and energy densities for the coin-cell supercapacitor were 69 W kg-1 and 6.6 Wh kg-1, respectively, while for the pouch cell, it was 7.4 W kg-1 and 1.0 Wh kg-1 , respectively. The coin-cell supercapacitor durability test was carried out for 1000 cycles, yielding the retention capacitance and coulombic efficiency values of 94-97% and 100%, respectively. These results showed that the performance of the supercapacitor is close to commercial products.
| Item Type: | Article |
|---|---|
| Subjects: | T Technology > TP Chemical technology |
| Divisions: | Fakultas Teknik (FT) > Prodi Teknik Kimia |
| Depositing User: | HERI Heri Rustamaji |
| Date Deposited: | 20 Jun 2023 08:09 |
| Last Modified: | 20 Jun 2023 08:09 |
| URI: | http://repository.lppm.unila.ac.id/id/eprint/52181 |
Actions (login required)
 |
View Item |