Nafrizal, Nafrizal and Tarkono, Tarkono and Sugiyanto, Sugiyanto (2011) Analisis Uji Destructive Dan Non Destructive Terhadap Uji sambungan LasV-Tunggal Baja AISI 1045. Mechanical Jurnal Ilmiah Teknik Mesin, 2 (2). pp. 25-31. ISSN 2087-1880
|
Text
@8. Jurnal mechanical Vol 2 2011.pdf - Submitted Version Download (681kB) | Preview |
Abstract
This paper reports the results of study on the strength behavior of welded joint both destructive and nondestructive testing. The parent metal choosen for the testing was AISI 1045 steel with main parameters of single-V welded form and horizontal welding position. The electrodes used for each parameters were AWS E-7016 LB-52 with diameter/amperes of 2.6 mm/80 Amp, 3.2 mm/110 Amp, and 4.0 mm/130 Amp. The specimens were nondestructively tested using the well-known radiography X-ray according to ASTM-1A for detecting welding flaws and its size. Tensile testing was performed to destructive based on the ASTM E-8 standard for tensile test. The results show that the tensile strength of the weld joint is reduction by about 28% compared to the parent metal without welding. The reduction in tensile strength is believed to be caused by welding defect, include porosity, inclusion, incomplete penetration, and reduction in carbon content from 0.5% in parent metal to about 0.1% in the welding region.
| Item Type: | Article |
|---|---|
| Uncontrolled Keywords: | smaw, tensile strength, welding defect |
| Subjects: | T Technology > TJ Mechanical engineering and machinery |
| Divisions: | Fakultas Teknik (FT) > Prodi Teknik Mesin |
| Depositing User: | Dr. SUGIYANTO ,M.T. |
| Date Deposited: | 31 Jul 2017 08:13 |
| Last Modified: | 31 Jul 2017 08:13 |
| URI: | http://repository.lppm.unila.ac.id/id/eprint/3742 |
Actions (login required)
 |
View Item |