Riyanto, Agus and Sembiring, Simon and Junaidi, Junaidi (2017) Karakteristik Fisis Aluminosilikat Geopolimer Berbasis Silika Sekam Padi untuk Aplikasi Fast Ionic Conductor. Reaktor, 17 (2). pp. 96-103. ISSN p-ISSN 0852 – 0798 e-ISSN 2407 – 5973


Download (1MB) | Preview
Official URL: http://ejournal.undip.ac.id/index.php/reaktor/arti...


The study aims to investigate the effect of calcination temperatures on the phase formation and electrical properties of aluminosilicate geopolymer prepared from rice husk silica and sodium aluminate. The samples were calcined at temperature from 150 to 550oC, the development of structures was characterized using xray difraction (XRD) and the electrical properties were measured by LCR meter. The result obtained indicated the significant role of calcining temperature on phase transformation of boehmite and quartz into aluminosilicate geopolymer, in which at calcining temperatures from 450 to 550oC, and the samples were dominated by semicrystal to amorphous phase which indicated that the aluminosilicate geoplymer has been formed. The presence of aluminosilicate geopolymer resulted in increased ionic electrical conductivity and dielectric loss factor as well as decrease dielectric constant. Ionic electrical conductivity of the calcined sample at 450oC is 4.49x10-5 S/cm at frequancy of 5x106 Hz, and XRD analysis demonstrated that the main structure is phase of semicrystal aluminosilicate geopolymer. Based on these character, the sample was considered is very suitable used to the fast ionic conductor materials.

Item Type: Article
Subjects: Q Science > QC Physics
Q Science > QD Chemistry
Divisions: Fakultas Matematika dan Ilmu Pengetahuan Alam (FMIPA) > Prodi Fisika
Depositing User: Agus Riyanto
Date Deposited: 31 Jul 2017 07:37
Last Modified: 31 Jul 2017 07:37
URI: http://repository.lppm.unila.ac.id/id/eprint/3726

Actions (login required)

View Item View Item