Badaruddin, Mohammad and Bakti, Bima and Prasetya, Budi and Sugiyanto, Sugiyanto (2021) Effect of austempering temperatures on surface hardness of AISI 4140 steel. IOP Conf. Series: Materials Science and Engineering, 1173 (1). pp. 1-7. ISSN 1757-899X

[img] Text
Badaruddin_2021_IOP_Conf._Ser.__Mater._Sci._Eng._1173_012027.pdf

Download (777kB)
Official URL: https://iopscience.iop.org/journal/1757-899X

Abstract

AISI 4140 steel is widely used in various engine elements, such as connecting rods,crankshafts, axles, piston rods, and sprockets. The purpose of this study was to determine the hardness value and microstructure using temperature ariations in the austempering process. The test results show that after the austempering process with temperature variations changed the hardness. The austempering process can increase the hardness value, but after the temperature is raised, the hardness value decreases. The greatest hardness value at 350°C was 264.4 BHN. After increasing the temperature to 400°C, the hardness decreased to 239.1 BHN. At a temperature of 450°C, the hardness was 226.7 BHN. Microstructure observations showed that the bainite is more uniform with increasing temperature. The test results show that the austempering temperature affects the hardness value and microstructure. When the austempering temperature is increased, the hardness value decreases

Item Type: Article
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Fakultas Teknik (FT) > Prodi Teknik Mesin
Depositing User: MOHAMMAD B
Date Deposited: 06 Nov 2021 05:37
Last Modified: 06 Nov 2021 05:37
URI: http://repository.lppm.unila.ac.id/id/eprint/35247

Actions (login required)

View Item View Item