Manurung, Posman and Marjunus, Roniyus (2020) Pengaruh Laju Penginjeksian Doping Fluor terhadap Aktivitas Fotokatalis Nanotitania Menggunakan Metode Sol Gel. Jurnal Teori dan Aplikasi Fisika, 8 (02). pp. 83-92. ISSN 2303-016X

	Text 117 Download (23kB)
	Text 1847 Download (34kB)
Preview	Text Pengaruh Laju Penginjeksian Doping Fluor terhadap Aktivitas.pdf Download (660kB) | Preview
Preview	Text Pengaruh Laju Penginjeksian Doping Fluor terhadap Aktivitas.pdf Download (660kB) | Preview

Abstract

The titania synthesis of fluorine doping (F-TiO2) was carried out through the sol-gel method. Titanium isopropoxide (TTIP), tween-80, isopropanol and ammonium fluoride (NH4F) as sources of doping fluorine were used as the main ingredients. This research aimed to study the effect of fluorine doping injection rate using injection pumps on F-TiO2 photocatalyst activity. Four fluorine doping samples were prepared with the respective penetration rate of 0.4 ml / 30 minutes; 0.4 ml / 60 minutes; 0.4 ml / 90 minutes and 0.4 ml / 120 minutes. The titania powder was calcined at 450 oC for 5 hours. The sintered sample was tested for photodegradation of remazol yellow under UV light. Physical characteristics were analyzed using transmission electron microscopy (TEM) and Uv-Vis spectrophotometer. The results of the UV-Vis spectrophotometer showed that the particle size of samples with an injection rate of 0.4 ml / 90 minutes showed higher photocatalyst activity with particle sizes of (14 nm ± 4 nm). Keywords: fluor doped, photodegradation, remazol yellow, titania

Item Type:	Article
Subjects:	Q Science > QC Physics
Divisions:	Fakultas Matematika dan Ilmu Pengetahuan Alam (FMIPA) > Prodi Fisika
Depositing User:	Mr Posman Manurung
Date Deposited:	19 Nov 2020 11:31
Last Modified:	19 Nov 2020 11:31
URI:	http://repository.lppm.unila.ac.id/id/eprint/26178

Actions (login required)

View Item