Mohammad, Badaruddin and Sugiyanto, Sugiyanto and Dwi, Asmi (2019) The resistance of an aluminide coating on a high-strength ASTM A29 steel subjected to a temperature of 850 °C. Materials Research Express, 6.

[img]
Preview
Text
Editorial Meyyappan 2014 Materials Research Express- P Badar.pdf

Download (336kB) | Preview
[img]
Preview
Text
JOurnal International 05-06-2019 dari P Badar.pdf

Download (1MB) | Preview
Official URL: https://doi.org/10.1088/2053-1591/ab2508

Abstract

An ASTM A29 steel was coated with aluminide by dipping in a molten Al bath at 700 °C for 16 s. The resistance of ASTM A29 steel to high-temperature oxidation drastically decreased upon oxidation at 850 °C for 12 h, whereas the oxidation resistance of the aluminised steel subjected to hot dipping was higher (by 25-fold). The external part of the aluminide layer, which consists of Fe2Al5, FeAl2, and FeAl (Cr, Si) phases scattered in the Fe2Al5 phase, was formed through the outward diffusion of Al and inward diffusion of Fe. The Fe2Al5 phase played an important role as a reservoir of Al atoms that form the alumina (Al2O3) scale, while Cr and Fe from the FeAl(Cr, Si) particles and accelerated the conversion of the metastable θ-Al2O3 phase to a stable α-Al2O3 phase. Consequently, the parabolic rate constants of aluminised steel decreased with extended oxidation time.

Item Type: Article
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Fakultas Teknik (FT) > Prodi Teknik Mesin
Depositing User: Dr. SUGIYANTO ,M.T.
Date Deposited: 14 Jun 2019 02:30
Last Modified: 14 Jun 2019 02:30
URI: http://repository.lppm.unila.ac.id/id/eprint/13363

Actions (login required)

View Item View Item