Badaruddin, Mohammad and Sugiyanto, Sugiyanto and Asmi, Dwi (2019) The resistance of an aluminide coating on a high-strength ASTM A29 steel subjected to a temperature of 850°C. Materials Research Express, 6 (8). pp. 1-8. ISSN 2053-1591

[img]
Preview
Text
mrx_6_8_0865d6.pdf

Download (1MB) | Preview
Official URL: https://iopscience.iop.org/journal/2053-1591

Abstract

AnASTM A29 steel was coated with aluminide by dipping in a molten Al bath at 700 °Cfor 16 s. The resistance ofASTMA29 steel to high-temperature oxidation drastically decreased upon oxidation at 850 °Cfor 12 h, whereas the oxidation resistance of the aluminised steel subjected to hot dipping was higher (by 25-fold). The external part of the aluminide layer, which consists of Fe2Al5, FeAl2, and FeAl (Cr, Si) phases scattered in the Fe2Al5 phase, was formed through the outward diffusion of Al and inward diffusion of Fe. The Fe2Al5 phase played an important role as a reservoir of Al atoms that form the alumina (Al2O3) scale, while Cr and Fe from the FeAl(Cr, Si) particles and accelerated the conversion of the metastable θ-Al2O3 phase to a stable α-Al2O3 phase. Consequently, the parabolic rate constants of aluminised steel decreased with extended oxidation time.

Item Type: Article
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Fakultas Teknik (FT) > Prodi Teknik Mesin
Depositing User: MOHAMMAD B
Date Deposited: 14 Jun 2019 02:30
Last Modified: 14 Jun 2019 02:30
URI: http://repository.lppm.unila.ac.id/id/eprint/13360

Actions (login required)

View Item View Item