Junaidi, Junaidi (2018) Concentration Effect of Silver Nanowires (AgNWs) Solution on The AgNWs Thin Films Fabricated Using Meyer-rod Coating. In: The 2nd International Conference on Applied Sciences Mathematics and Informatics, 9-11 Agustus 2018, Hotel Horison, Bandar Lampung, Indonesia. (In Press)

[img] Text
ICASMI 2018.pdf

Download (698kB)

Abstract

In this paper, we report our investigation effect of concentration of silver nanowires (AgNWs) solution on the AgNWs thin films coated onto a glass substrate by simple Meyer-rod coating. Diameter and length of AgNWs were used about 120 nm and 20 to 30 µm, respectively. Concentration of AgNWs were variated of 186 mg/ml, 210 mg/ml, and 223 mg/ml in ethanol solution. AgNWs thin films then were heated at temperature 90 o C for 20 min. The UV-vis spectrophotometry, scanning electron microscope (SEM), and four-point-probe were employed to characterize the AgNWs thin films. The result shows that concentration of AgNWs solution affects on the transmittance and a sheet resistance of the AgNWs thin films. The transmittance at the wavelength of 550 nm is obtained 94.5% by a sheet resistance about 1 . 2 Ω/ sq. The higher concentration of AgNWs solution can decrease the sheet resistance and the transparency of the AgNWs thin films.

Item Type: Conference or Workshop Item (Paper)
Subjects: Q Science > QC Physics
Divisions: Fakultas Matematika dan Ilmu Pengetahuan Alam (FMIPA) > Prodi Fisika
Depositing User: Dr. JUNAIDI
Date Deposited: 16 Nov 2018 17:32
Last Modified: 16 Nov 2018 17:32
URI: http://repository.lppm.unila.ac.id/id/eprint/10074

Actions (login required)

View Item View Item